1. Apa teknik analisis metalurgi yang mendiagnosis kegagalan tabung?
Pemindaian Mikroskop Elektron (SEM) mengungkapkan morfologi permukaan fraktur . spektroskopi sinar-X-ray yang dispersif energi (eds) mengidentifikasi elemen korosif . pengujian kekerasan, mendeteksi coriran {{{4} {3} {{4} {{4} {{4} {{{4} {{4} {{4} {{{4} {{{4} {{4 {{4 {{4 {{4 {{4 {{4 {{4 {4 {{4 {{4 {4 { korosi .
2. Bagaimana Anda membedakan antara kegagalan overheating jangka pendek dan jangka panjang?
Short-term overheating shows thin-lipped, ductile rupture with minimal scaling. Long-term creep failures exhibit thick oxide layers and macroscopic cavitation. Microstructural analysis reveals pearlite spheroidization in prolonged cases. Fracture surfaces differ in oxidation patterns. Temperature history reconstruction membantu mengonfirmasi mode kegagalan .
3. Apa tanda -tanda karakteristik kerusakan hidrogen dalam tabung boiler?
Brittle fractures with minimal deformation near welds or bends. Under-microscope examination shows intergranular cracking. Blistering may appear on internal surfaces. Associated with low pH water chemistry conditions. Often accompanies caustic corrosion in high-stress areas.
4. Bagaimana analisis mikrostruktur memprediksi masa pakai tabung yang tersisa?
Laju kasar karbida menunjukkan akumulasi kerusakan creep . pengukuran ketebalan skala oksida memperkirakan waktu-pada-suhu . batas oksidasi butir yang berkorelasi dengan paparan layanan . {Parameter yang tersisa untuk penilaian hidup yang tersisa (RLA) model {{{{{{{{{{{{{{{{{{{{{{{{{{{{{{{{{{{{{{{{{{{{{{{{{yang tersisa {{{{{{{{5) perbaikan .
5. Dokumentasi apa yang penting untuk penyelidikan kegagalan yang tepat?
Log operasional yang mencakup 30 hari sebelum kegagalan . catatan pengolahan air termasuk dosis kimia . riwayat pemeliharaan komponen yang gagal . sebagai sertifikasi material yang terpaku . fotografi dari situs kegagalan sebelum gangguan {6}